WEICON Fast-Metal Minute Adhesive
- with a high solids content, pasty
- very short pot life, fast-curing
- gap-filling, residual elasticity
WEICON Fast-Metal Minute Adhesive is ideal for repairs and bondings with larger bonding gaps or bigger tolerances. The gap filling properties make it suitable for rough and poorly fitting surfaces but also to fill in cracks, cavities and unlevelled surfaces.
Fast-Metal Minute Adhesive can be used on numerous materials such as metal, plastic, fibre reinforced materials, ceramics, glass, stone and wood.
ISSA: 75.629.51
IMPA: 81 29 81
| Technical Data | |
|---|---|
| Basis | epoxy resin |
| Nature | paste consistency, crack-filler |
| Supplied in | double syringe |
| Content | 24 ml |
| Mixing ratio by volume (Resin/Hardener) | 1 : 1 |
| Pot life with 10 ml material at +20°C | 3-4 Min. |
| Density of the mixture | 1,80 g/cm³ |
| Viscosity of the mixture at +20°C | 300.000 mPa·s |
| Processing temperature | +10 bis +30 °C |
| Curing temperature | +6 bis +40 °C |
| Colour | grey |
| Gap covering power to max. | 4 mm |
| Handling strength (35% strength/+20°C) after | 40 Min. |
| Capable of bearing mechanical loads(50% strength/+20°C) after | 2 h |
| Final strength (100% strength/+20°C) after | 1 day(s) |
| Pressure | 10 MPa |
| Tensile | 24 MPa |
| Torsion | 58 MPa |
| Shore hardness D | 70 |
| Steel, sand-blasted | 20 N/mm² |
| Aluminium, sand-blasted | 19 N/mm² |
| Rigid PVC, roughened | 11 N/mm² |
| Temperature resistance | -50 bis +145 °C |